Percorrer por autor "Ramos, Rui"
A mostrar 1 - 5 de 5
Resultados por página
Opções de ordenação
- Análise termomecânica de perfis enformados a frioPublication . Mesquita, L.M.R.; Mendonça, Miguel; Ramos, Rui; Barreira, Luísa; Piloto, P.A.G.This work presents an experimental study about cold formed steel elements submitted to compression loads. The sections analyzed are C and Z sections made of steel sheet with 1.5 and 2 [mm] thick and three different cross section heights. The compression tests were made at ambient and elevated temperatures. In both cases a pined support was developed and used. The member resistance at ambient temperature was determined by applying an increasing compression load until the member collapse was achieved. The fire tests were performed in a fire resistance furnace, using the same type of end supports, and a mechanical load given by a specific degree of utilization that is maintained constant during the fire test. These tests allow the determination of the fire resistance time and member critical temperature. The experimental results are compared with the ones obtained with the Eurocode simplified models.
- Análise termomecânica de perfis enformados a frioPublication . Mendonça, Miguel; Ramos, Rui; Mesquita, L.M.R.Os perfis enformados a frio têm uma grande aplicação em estruturas de aço leve (“lightsteelframing”), nomeadamente em edifícios, devido à sua leveza e resistência mecânica específica. Tratando-se de elementos estruturais de parede fina, são em geral classificados como secções de classe 4 segundo o Eurocódigo 3, parte1 e sujeitos a fenómenos de instabilidade local, distorcional e global, ou uma interação destes três modos. Quando expostos a uma condição de incêndio atingem o colapso a baixas temperaturas, traduzindo-se num baixo tempo de resistência ao fogo. Este trabalho aborda o comportamento térmico e mecânico de perfis de aço enformados a frio através de um estudo experimental à temperatura ambiente e simultaneamente em condições de incêndio. São analisadas secções C e Z com espessuras de chapa de 1.5 e 2[mm] e três alturas da secção distintas. A capacidade resistente dos perfis é determinada à temperatura ambiente por um conjunto de 12 testes através da aplicação de uma força de compressão continuamente crescente até se atingiro colapso do elemento. Em situação de incêndio são realizados 24 testes num forno de resistência ao fogo, apresentado na Figura 1, nos quais o elemento estrutural é submetido a um carregamento mecânico constante, representativo de um grau de utilização, e simultaneamente ao fogo através da curva de incêndio padrão. Estes ensaios permitem a determinação do tempo de resistência ao fogo e da temperatura crítica dos perfis ensaiados. Os resultados são comparados com aqueles provenientes dos modelos simplificados do Eurocódigo 3, verificando-se que, tendencialmente, os obtidos pelos modelos simplificados são em geral superiores aos obtidos nos ensaios experimentais, como se apresenta na Figura 1.
- Análise termomecânica de perfis enformados a frioPublication . Mesquita, L.M.R.; Mendonça, Miguel; Ramos, Rui; Barreira, Luísa; Piloto, P.A.G.This work presents an experimental study about cold formed steel elements submitted to compression loads. The sections analyzed are C and Z sections made of steel sheet with 1.5 and 2 [mm] thick and three different cross section heights. The compression tests were made at ambient and elevated temperatures. In both cases a pined support was developed and used. The member resistance at ambient temperature was determined by applying an increasing compression load until the member collapse was achieved. The fire tests were performed in a fire resistance furnace, using the same type of end supports, and a mechanical load given by a specific degree of utilization that is maintained constant during the fire test. These tests allow the determination of the fire resistance time and member critical temperature. The experimental results are compared with the ones obtained with the Eurocode simplified models.
- Comportamento ao fogo de perfis C e Z enformados a frioPublication . Mesquita, L.M.R.; Mendonça, Miguel; Ramos, Rui; Barreira, Luísa; Piloto, P.A.G.Este trabalho apresenta um estudo paramétrico realizado em perfis enformados a frio de secção transversal C e Z de diferentes alturas da secção e de espessura da chapa de aço. A análise é realizada através de ensaios à temperatura ambiente e num forno de resistência ao fogo em condições de incêndio. Os resultados da capacidade resistente, do tempo de resistência ao fogo e da temperatura crítica, são comparados com os resultados dos modelos simplificados do Eurocódigo 3, partes 1.2 e 1.3, verificando-se que, tendencialmente, os obtidos pelos modelos simplificados são em geral superiores aos obtidos nos ensaios experimentais.
- Thermomechanical analysis of cold formed steel sectionsPublication . Mesquita, L.M.R.; Mendonça, Miguel; Ramos, Rui; Barreira, Luísa; Piloto, P.A.G.This work presents an experimental study about cold formed steel elements submitted to compression loads. The sections analyzed are C and Z sections made of steel sheet with 1.5 and 2 [mm] thick and three different cross section heights. The compression tests were made at ambient and elevated temperatures. In both cases a pined support was developed and used. The member resistance at ambient temperature was determined by applying an increasing compression load until the member collapse was achieved. The fire tests were performed in a fire resistance furnace, using the same type of end supports, and a mechanical load given by a specific degree of utilization that is maintained constant during the fire test. These tests allow the determination of the fire resistance time and member critical temperature. The experimental results are compared with the ones obtained with the Eurocode simplified models.